Product Feature
Selected high quality natural inorganic mineral raw materials
Easy kneading and pressing adjustment, simple construction, saving space loss
Strong bonding of various types of low water absorption tiles
Strong viscosity, ready to use with water, strong weather resistance
Construction Technology
With a tooth-shaped scraper will be applied to the slurry on top of the work surface, so that it is evenly distributed, and into a strip of teeth.
About 1 square meter each time (depending on the weather temperature, the construction temperature range of 5 ~ 40 ℃), and then in 5 ~ 15 minutes will be kneaded on the tiles can be (adjustments need to be made in 20 ~ 25 minutes).
Selection of teeth scraper size should take into account the flatness of the work surface and the convexity of the back of the tiles; pay attention to retain the expansion joints.
After the completion of tiling, must wait until the mastic completely dry and solid (about 24 hours) before the next step of the caulking process; not dry and solid before the use of a damp cloth or sponge to clean the surface of the tiles (and tools).
If curing more than 24 hours, the tile surface stains can be cleaned with tile stone cleaner (do not use acidic cleaners)
C2TES1
Classification | Performance | Index |
C2TES1-Enhanced cement base adhesive
| Tensile bond strength/MPa | ≥1.0 |
Tensile bond strength after immersion/MPa | ≥1.0 | |
Tensile bond strength after thermal aging/MPa | ≥1.0 | |
Tensile bond strength after freeze-thaw cycle/MPa | ≥1.0 | |
Drying time ≥20min, tensile bond strength/MPa | ≥0.5 | |
Slippage/mm | ≤0.5 | |
Longer drying time ≥30min, tensile bond strength/MPa | ≥0.5 | |
Flexible adhesive(S1)/mm | ≥2.5，<5 |
C2TES2
Classification | Performance | Index |
C2TES2-Enhanced cement base adhesive
| Tensile bond strength/MPa | ≥1.0 |
Tensile bond strength after immersion/MPa | ≥1.0 | |
Tensile bond strength after thermal aging/MPa | ≥1.0 | |
Tensile bond strength after freeze-thaw cycle/MPa | ≥1.0 | |
Drying time ≥20min, tensile bond strength/MPa | ≥0.5 | |
Slippage/mm | ≤0.5 | |
Longer drying time ≥30min, tensile bond strength/MPa | ≥0.5 | |
High flexible adhesive(S2)/mm | ≥5 |